Canvases of super thin basalt fiber (STBF)

holst

Canvases represent a layer of randomly arranged super thin basalt fibers, which are held together by natural cohesion forces.
Basalt canvases are made of raw basalt without additional charging, which makes their properties completely unique.
Canvases of super thin basalt fiber (STBF) do not contain phenol-formaldehyde binder, whose presence is obvious in many other mineral products. The average diameter of the "Magmawool" super thin basalt fiber is 1.2 microns.
Thus, the quality of super thin basalt fiber produced by the "Magma Industry" company measures up to the world's best examples of insulating materials and even exceeds them in many ways.

Features:

  • excellent thermal insulation and sound-absorbing characteristics;
  • non-flammable, fire-resistant, fire-proof;
  • environmentally friendly (does not contain phenol-formaldehyde binder);
  • defies the aging process (service life is more than 50 years);
  • resistance to microorganisms and rodents, do not rot;
  • do not increase diffuse resistance of constructions (excellent water vapor permeability);
  • has a low hygroscopic (does not absorb moisture from the air);
  • excellent mechanical properties (vibration resistance);
  • chemical resistance to oils, acids, alkali;
  • wide temperature range of application.

Application area:

  • thermal and acoustic insulation of floors, ceilings between the joists;
  • acoustic insulation of lofts, attics, ceilings and intermediate floors;
  • thermal insulation of high-temperature furnaces, pipelines, boilers, water heaters;
  • fire protection of building structures;
  • thermal insulation in shipbuilding, water parks, swimming pools, saunas;
  • thermal insulation of tanks for liquids transportation;
  • thermal insulation at nuclear and thermal power stations (does not accumulate radiation).
Технические характеристики(БСТВ):
Свойства Параметр Единица измерения
Средний диаметр волокна, не более 2 мкм
Массовая доля неволокнистых включений "корольков" размером свыше 0,25% до 4,8 %
Размеры (Длинна х Ширина х Толщина) 1000...6000 х 1200 х 30...100 мм
Плотность от 23 до 200 кг/м3
Коэффициент теплопроводности, не более:
при (25±5)°С 0,034 Вт/м*К
при (125±5)°С 0,054 Вт/м*К
при (300±5)°С 0,098 Вт/м*К
Коэффициент звукопоглощения, для частот от 100 до 2000 Гц 0,95 - 0,99 -
Температурный интервал применения -269...+900 °С
Температура спекания волокон +1100 °С
Гигроскопичность 0,2 - 0,3 %
Горючесть НГ (не горючий) ДСТУ Б В.2.7-94-2000 (ГОСТ 4640-93)
Модуль кислотности 4,8 - 5,2 -
Массовая доля влаги, не более 0,8 %
Массовая доля паров хлора, не более 0,03 %
Химическая устойчивость (потеря веса в % при 3-часовом кипячении):
в воде 0,6 %
в щелочной среде 2,75 %
в кислотной среде 2,2 %
Выщелачиваемость в пересчете на Na2O на 5000 см3, не более 5,0 %
Наличие связующего нет